Properties |
Test
Method |
Unit |
2200J |
| Melt
Flow Rate (MFR) 190 °C |
ASTM
D-1238 |
g/10min |
5.0 |
| Mold
Shrinkage |
HPC
Method |
% |
1.8 |
| Density |
ASTM
D-1505 |
g/cm3 |
0.965 |
| Softening
Point |
ASTM
D-1525 |
°C |
124 |
| Tensile
Strength at Yield |
ASTM
D-638 |
Kg/cm2 |
260 |
| Ultimate
Elongation |
ASTM
D-638 |
% |
>300 |
| Heat
Distortion Temperature |
ASTM
D-648 |
°C |
78 |
| Flexural
Modulus of Elasticity |
ASTM
D-790 |
Kg/cm2 |
14000 |
| Hardness
(Rockwell) |
ASTM
D-785 |
R |
68 |
| Du-Pont
Impact Strength (23°C) |
HPC
Method |
Kg-cm |
100 |
| IZOD
Impact Strength (23°C) |
ASTM
D-256 |
Kg-cm/cm |
10 |
| ESCR |
ASTM
D-1693 |
F 50HR |
5 |