Properties	Test Method	Unit	2700J
Melt Flow Rate (MFR) 190 °C	ASTM D-1238	g/10min	7.0
Mold Shrinkage	HPC Method	%	1.8
Density	ASTM D-1505	g/cm³	0.949
Softening Point	ASTM D-1525	°C	120
Tensile Strength at Yield	ASTM D-638	Kg/cm²	200
Ultimate Elongation	ASTM D-638	%	>300
Heat Distortion Temperature	ASTM D-648	°C	69
Flexural Modulus of Elasticity	ASTM D-790	Kg/cm²	8,000
Hardness (Rockwell)	ASTM D-785	R	60
Du-Pont Impact Strength (23°C)	HPC Method	Kg-cm	100
IZOD Impact Strength (23°C)	ASTM D-256	Kg-cm/cm	11
ESCR	ASTM D-1693	F 50HR	11