Properties |
Test
Method |
Unit |
J-370 |
| Melt
Flow Rate (MFR) 230 °C |
ASTM
D-1238 |
g/10min |
35.0 |
| Mold
Shrinkage |
HPC
Method |
% |
1.50 |
| Density |
ASTM
D-1505 |
g/cm3 |
0.9 |
| Tensile
Strength at Yield |
ASTM
D-638 |
Kg/cm2 |
280 |
| Ultimate
Elongation |
ASTM
D-638 |
% |
>100 |
| Flexural
Modulus of Elasticity |
ASTM
D-790 |
Kg/cm2 |
15,000 |
| Hardness
(Rockwell) |
ASTM
D-785 |
R |
97 |
| IZOD
Impact Strength (23 °C) |
ASTM
D-256 |
Kg-cm/cm |
5.5 |
| IZOD
Impact Strength (-10 °C) |
ASTM
D-256 |
Kg-cm/cm |
2.5 |
| Du-Pont
Impact Strength(23 °C) |
HPC
Method |
Kg-cm |
35 |
| Heat
Distortion Temperature (4.6Kgf) |
ASTM
D-648 |
°C |
114 |
| Flammability |
UL |
- |
HB |
Industry
Info