Properties |
Test
Method |
Unit |
SB-520 |
| Melt
Flow Rate (MFR) 230 °C |
ASTM
D-1238 |
g/10min |
1.8 |
| Density |
ASTM
D-1505 |
g/cm3 |
0.9 |
| Tensile
Strength at Yield |
ASTM
D-638 |
Kg/cm2 |
270 |
| Ultimate
Elongation |
ASTM
D-638 |
% |
500< |
| Flexural
Modulus of Elasticity |
ASTM
D-790 |
Kg/cm2 |
10,000 |
| Hardness
(Rockwell) |
ASTM
D-785 |
R |
87 |
| IZOD
Impact Strength (23°C) |
ASTM
D-256 |
Kg-cm/cm |
11 |
| Softening
Point |
ASTM
D-1525 |
°C |
135 |
| Heat
Distortion Temperature |
ASTM
D-648 |
°C |
103 |
| Du-Pont
Impact Strength (23°C) |
HPC
Method |
Kg-cm |
60 |
| HAZE
(2mm) |
ASTM
D-746 |
% |
30 |
| Mold
Shrinkage |
HPC
Method |
% |
1.80 |