Honam
Petrochemical Corporation |
|
HDPE - SFR-171H |
|
Properties |
Test
Method |
Unit
|
SFR-171H |
| Melt
Flow Rate (MFR) 230 °C |
ASTM
D-1238 |
g/10min |
35.0 |
| Mold
Shrinkage |
HPC
Method |
% |
1.6 |
| Density |
ASTM
D-1505 |
g/cm3 |
0.9 |
| Tensile
Strength at Yield |
ASTM
D-638 |
Kg/cm2 |
340 |
| Ultimate
Elongation |
ASTM
D-638 |
% |
500< |
| Flexural
Modulus of Elasticity |
ASTM
D-790 |
Kg/cm2 |
15,000 |
| Hardness
(Rockwell) |
ASTM
D-785 |
R |
100 |
| IZOD
Impact Strength (23 °C) |
ASTM
D-256 |
Kg-cm/cm |
2.7 |
| Softening
Point |
ASTM
D-1525 |
°C |
154 |
| Heat
Distortion Temperature |
ASTM
D-648 |
°C |
114 |
|
Major Characteristics
- High processability and high speed
- Suitable for the processing-at high spinning
speed - of fibers
- Non-woven fabrics
Application
- Suitable for spun bonded diaper
- Underware and hygienic clothing
- Non-woven fabrics
|
|
|
|