 Industry
Info |
|
|
Hyosung
PP |
|
Random
Copolymer |
|
Product
Properties |
|
TYPICAL PROPERTY |
TEST METHOD |
UNIT |
R601 |
R701 |
R801 |
R801H |
| Melt Index |
ASTM D1238 |
g/10 min |
10 |
18 |
30 |
30 |
| Tensile
Strength (Yield) |
ASTM D638 |
kg/cm² |
310 |
310 |
300 |
310 |
| Elongation
(Break) |
ASTM D638 |
% |
500 |
500 |
500 |
500 |
| Flexural Modulus |
ASTM D790 |
kg/cm² |
11,000 |
11,000 |
10,500 |
11,000 |
| Izod |
23ºC |
ASTM D256 |
kg.cm/cm |
6.5 |
6.0 |
5.0 |
6.0 |
| 0ºC |
4.0 |
3.5 |
3.0 |
4.0 |
| Impact Strenght |
-20ºC |
- |
- |
- |
- |
| Rockwell Hardness |
ASTM D785 |
R-Scale |
90 |
90 |
90 |
88 |
| Vicat Softening Point |
ASTM D1525 |
ºC |
135 |
135 |
135 |
133 |
| Heat Deflection
Temperature(4.6kg/cm²) |
ASTM D648 |
ºC |
100 |
100 |
100 |
98 |
| Applications |
High transparence products
ISBM (Injection stretch blow Molding)
bottles |
| Characteristics |
High transparency/Stiffness |
|
TYPICAL PROPERTY |
TEST METHOD |
UNIT |
R300H |
R600F |
| Melt Index |
ASTM D1238 |
g/10 min |
2.0 |
11 |
| Tensile
Strength (Yield) |
ASTM D638 |
kg/cm² |
220 |
240 |
| Elongation
(Break) |
ASTM D638 |
% |
- |
- |
| Flexural Modulus |
ASTM D790 |
kg/cm² |
7,500 |
8,000 |
Izod
Impact Strength |
23ºC |
ASTM D256 |
kg.cm/cm |
- |
- |
| 0ºC |
- |
- |
| -20ºC |
- |
- |
| Rockwell Hardness |
ASTM D785 |
R-Scale |
- |
- |
| Vicat Softening Point |
ASTM D1525 |
ºC |
- |
- |
| Heat Deflection
Temperature(4.6kg/cm²) |
ASTM D648 |
ºC |
65 |
  |
| Melting Point |
HYOSUNG Method |
ºC |
139 |
148 |
| Heat Sealing Temperature |
HYOSUNG Method |
ºC |
119 |
  |
| Applications |
Shrink films |
Inflation films |
| Characteristics |
Shrink ability |
High transparency, High slip |
|
TYPICAL PROPERTY |
TEST METHOD |
UNIT |
R200P |
R301 |
R401 |
| Melt Index |
ASTM D1238 |
g/10 min |
0.20 |
1.5 |
4.0 |
| Tensile
Strength (Yield) |
ASTM D638 |
kg/cm² |
270 |
310 |
310 |
| Elongation
(Break) |
ASTM D638 |
% |
500 |
500 |
500 |
| Flexural Modulus |
ASTM D790 |
kg/cm² |
8,500 |
11,000 |
11,000 |
Izod
Impact Strength |
23ºC |
ASTM D256 |
kg.cm/cm |
N.B |
9.0 |
7.5 |
| 0ºC |
- |
- |
- |
| -20ºC |
- |
- |
- |
| Rockwell Hardness |
ASTM D785 |
R-Scale |
75 |
90 |
90 |
| Vicat Softening Point |
ASTM D1525 |
ºC |
120 |
135 |
135 |
Heat Deflection
Temperature(4.6kg/cm²) |
ASTM D648 |
ºC |
95 |
100 |
100 |
| Applications |
Under floor, Water service
pipes |
Blow
molding |
High
transparent
sheets |
| Characteristics |
Pressure resistance
Flexibility |
High transparency
Stretchability |
High transparency
Stiffness |
|
|
|
|