 Industry
Info |
|
|
Hyosung
PP |
|
Special
Purpose Homopolymer |
|
Product
Properties |
|
TYPICAL PROPERTY |
TEST METHOD |
UNIT |
J700-1 |
S800 |
J800R |
J801 |
J801R |
| Melt Index |
ASTM D1238 |
g/10 min |
11 |
18 |
18 |
18 |
18 |
| Tensile
Strength (Yield) |
ASTM D638 |
kg/cm² |
400 |
380 |
380 |
420 |
420 |
| Elongation
(Break) |
ASTM D638 |
% |
500 |
500 |
500 |
300 |
300 |
| Flexural Modulus |
ASTM D790 |
kg/cm² |
18,500 |
18,000 |
18,000 |
20,000 |
20,000 |
Izod
Impact Strength |
23ºC |
ASTM D256 |
kg.cm/cm |
3.5 |
2.5 |
2.5 |
4.0 |
4.0 |
| 0ºC |
2.5 |
2.0 |
2.0 |
2.0 |
2.0 |
| -20ºC |
- |
- |
- |
- |
- |
| Rockwell
Hardness |
ASTM D785 |
R-Scale |
110 |
100 |
100 |
115 |
115 |
| Vicat Softening Point |
ASTM D1525 |
ºC |
155 |
155 |
155 |
155 |
155 |
Heat Deflection
Temperature(4.6kg/cm²) |
ASTM D648 |
ºC |
125 |
120 |
120 |
130 |
130 |
| Applications |
Disposable syringe
Houseware
Appliances |
Houseware Appliances |
Disposable
syringe
Transparency products
Appliances |
| Characteristics |
High stiffness
Fast cycle High slip |
Heat resistance
UL 94HB |
Long term
Heat resistance
UL746B(120¡É)
UL 94HB |
heat resistance
UL 94HB |
Long term
heat resistance
UL746B(120¡É)
UL 94HB |
|
TYPICAL PROPERTY |
TEST METHOD |
UNIT |
F801L |
B200 |
| Melt Index |
ASTM D1238 |
g/10 min |
25 |
0.4 |
| Tensile
Strength (Yield) |
ASTM D638 |
kg/cm² |
250 |
390 |
| Elongation
(Break) |
ASTM D638 |
% |
500 |
500 |
| Flexural Modulus |
ASTM D790 |
kg/cm² |
11,000 |
17,000 |
Izod
Impact Strength |
23ºC |
ASTM D256 |
kg.cm/cm |
4.0 |
7.0 |
| 0ºC |
3.0 |
4.0 |
| -20ºC |
- |
- |
| Rockwell Hardness |
ASTM D785 |
R-Scale |
85 |
100 |
| Vicat Softening Point |
ASTM D1525 |
ºC |
135 |
155 |
Heat Deflection
Temperature(4.6kg/cm²) |
ASTM D648 |
ºC |
90 |
110 |
| Applications |
Bag Lamination |
Vacuum forming
Blow molding |
| Characteristics |
High adhesion Low neck-in |
High stiffness |
|
|
|
|
|