REPOL (POLYPROPYLENE)

REPOL - H030SG (HOMOPOLYMER)

Product Description and Applications

REPOL Polypropylene H030SG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity and stereo specificity of the SHAC catalyst system.

REPOL H030SG is recommended for raffia tapes used in making woven fabrics for sacking, carpet backing,industrial fabric and geotextile applications. UV-Stabilized version of this grade (H030SU) is also available for outdoor applications.

Features

Repol H030SG is designed to provide :

High tenacity in tapes
Consistent processabillity
Low "water carryover"
Good colour and processing stability

Typical properties of REPOL H030SG are as follows
Property	ASTM Test Method	Unit	*Typical Value.**
Melt flow index,(230oc/2.16Kg)	D 1238	g/10 min	3.0
Tensile Strength at yield (50 mm/min )	D 638$	MPa	35
Elongation at yield (50 mm/min )	D 638$	%	10
Flexural modulus (1% secant)	D 790A$	MPa	1650
Notched izod impact strength (23oc)	D 256$	J/m	40
Heat deflection temperature (455kPa)	D 648	oC	104

$ : ASTM D638 Type I specimen injection moulded and tested in accordance with ASTM D4101.

Repol H030SG meets the requirements stipulated in IS 10910-1984 on on "Specification for Polypropylene and its copolymers for safe use in contact with foodstuffs, pharmaceuticals, and drinking water". Additives incorporated in this grade conform to the positive list of constituents as prescribed in IS-10909-1984.The grade and the additives incorporated in it also comply with the FDA:CFR Title 21, 177.1520, Olefin polymers.

REPOL is the registered trademark for Polypropylene from Reliance Industries Limited

*Typical values with injection moulded specimens, not to be taken as specification
The data, information and suggestions contained contained herein are given purely as a guide. Reliance Industries Limited and Reliance Group Companies undertake no responsibility either for the results deriving from their adoption or for possible position in apparent contrast with existing patent rights.