REPOL (POLYPROPYLENE)

REPOL - H350FG (HOMOPOLYMER)

Product Description and Applications

REPOL Polypropylene H350FG is manufactured using Unipol PP process which combines the production efficiency of gas phase fluidized bed reactor technology with the high activity and stereo specificity of the SHAC catalyst system.

REPOL H350FG is recommended for use incompact spinning operations for making multifilament fine denier multifilament yarn and nonwovens.

Features

Repol H350FG is designed to provide
  • Good spinning characteristics
  • Consistent processabillityat highl ine speeds
  • Good colour stability
  • Good flow behaviour

Typical properties of REPOL H350FG are as follows

Property
ASTM Test Method
Unit
Typical Value*.
Melt flow index,(230oc/2.16Kg)
D 1238
g/10 min
35.0
Tensile Strength at yield (50 mm/min )
D 638$
MPa
34
Elongation at yield (50 mm/min )
D 638$
%
10
Flexural modulus (1% secant)
D 790A$
MPa
1650
Notched izod impact strength (23oc)
D 256$
J/m
22
Heat deflection temperature (455kPa)
D 648
oC
104
$ : ASTM D638 Type I specimen injection moulded and tested in accordance with ASTM D4101.

Repol B120MA meets the requirements stipulated in IS 10910-1984 on on "Specification for Polypropylene and its copolymers for safe use in contact with foodstuffs, pharmaceuticals, and drinking water". Additives incorporated in this grade conform to the positive list of constituents as prescribed in IS-10909-1984.The grade and the additives incorporated in it also comply with the FDA:CFR Title 21, 177.1520, Olefin polymers.
REPOL is the registered trademark for Polypropylene from Reliance Industries Limited

* Typical values with injection moulded specimens, not to be taken as specification
The data, information and suggestions contained contained herein are given purely as a guide. Reliance Industries Limited and Reliance Group Companies undertake no responsibility either for the results deriving  from their adoption or for possible position in apparent contrast with existing patent rights.